Product details
Material：Mo1,MoLa,TZM
Composition：Mo1:≥99.95%
MoLa:Mo + La2O3(0.5%～1%)
TZM: Mo + 0.40～0.55%Ti + 0.06～0.12%Zr + 0.01～0.043% C
Standard：ASTM B 386,GB/T 3876-2017
Size：(0.03～50)X(10～750)X3000mm
Product performance: Molybdenum plate, sheet are cross-rolled in the production process, and the stress is removed by vacuum annealing, so it has the advantages of high strength, high temperature resistance, uniform internal structure, good processing performance, high temperature creep resistance and so on.
Molybdenum block after hot isostatic pressing has high density, fine grain and it’s suitable for deep processing. In addition to pure Mo products, Chenjun Tungsten & Molybdenum Technology can also supply MoLa, TZM, WMo alloy products.
Specification:
Custom sizes available upon request. Your special requests are available.
Name | Thickness (mm) | Width (mm) | Length (mm) | Surface |
Mo plate | >2 | 10～600 | 100～2500 | Ground, Alkaline cleaning, Cold rolling |
Mo sheet | 0.1～2 | 10～750 | 100～3000 | Alkaline cleaning, Cold rolling |
Mo foil/belt | 0.03～0.1 | 50～150 | ------ | Cold rolling |
Forged Mo block/disk | Weight for each one≤100Kg | Ground | ||
Process flow:
Mo plate/sheet:
Powder--Pressing--Sintering--Rolling--Surface treatment--Heat treatment --Finished
Products--Inspection--Packing
Mo Block/ disk:
Powder--Pressing--Sintering--Forging--Surface treatment--Heat treatment --Finished
Products--Inspection--Packing
Applications:
-- Used as heat insulation screen and cover plate in sapphire crystal furnace
-- Used as reflection screen, heating belt and connecting parts in vacuum furnace
-- Used for producing Mo sputtering target
-- Used for processing high temperature Mo boat or Mo box
-- Used for procssing shield,screen, hook and other accessories in the monocrystalline silicon furnace
-- Used for processing heating elements and high temperature structural parts
-- Used for processing ion implantation parts